TPE美國杜邦4069 高性能級

TPE美國杜邦4069的詳細描述：

DuPont Performance Polymers Hytrel? 4069 TPC-ET (Unverified Data**) 物性表

物理性能額定值 (公制)額定值 (英制)測試方法比重1.11 g/cc1.11 g/ccASTM D792密度1.11 g/cc0.0401 lb/in3ISO 1183Water Absorption0.20 %

@Temperature 23.0 °C

0.20 %

@Temperature 73.4 °F

Equilibrium 50%RH; ISO 62
0.70 %

@Temperature 23.0 °C

0.70 %

@Temperature 73.4 °F

Immersion 24h; ASTM D570
0.70 %

@Temperature 23.0 °C

Immersion 24h; ISO 62
0.70 %

@Temperature 23.0 °C

Saturation, immersed; ISO 62線性成型收縮率0.0080 cm/cm0.0080 in/inFlow; ASTM D955線性成型收縮率,Flow0.0080 cm/cm

@Thickness 2.00 mm

0.0080 in/in

@Thickness 0.0787 in

ISO 294-4線性成型收縮率，橫向0.0080 cm/cm

@Thickness 2.00 mm

ISO 294-4熔體流動速率8.5 g/10 min

@Load 2.16 kg, Temperature 220 °C

8.5 g/10 min

@Load 4.76 lb, Temperature 428 °F

ASTM D1238
8.5 g/10 min

@Load 2.16 kg, Temperature 220 °C

ISO 1133化合物熔體指數(shù)7.7 g/10 min

@Load 2.16 kg, Temperature 220 °C

7.7 g/10 min

@Load 4.76 lb, Temperature 428 °F

cm3/10 min; ISO 1133機械性能額定值 (公制)額定值 (英制)測試方法肖氏硬度 (邵氏 D)= 300 %

@Temperature 73.4 °F

ISO 527 (1BA bar)
650 %

@Temperature 23.0 °C

650 %

@Temperature 73.4 °F

ISO 527 (1BA bar)
700 %

@Temperature 23.0 °C

700 %

@Temperature 73.4 °F

ASTM D638
800 %

@Temperature 23.0 °C

800 %

@Temperature 73.4 °F

nominal; ISO 527 (1BA bar)拉伸模量0.0450 GPa

@Temperature 23.0 °C

6.53 ksi

@Temperature 73.4 °F

ISO 527彎曲模量0.0280 GPa

@Temperature 100 °C

4.06 ksi

@Temperature 212 °F

ASTM D790
0.0280 GPa

@Temperature 100 °C

ISO 178
0.0470 GPa

@Temperature 23.0 °C

6.82 ksi

@Temperature 73.4 °F

ISO 178
0.0550 GPa

@Temperature 23.0 °C

7.98 ksi

@Temperature 73.4 °F

ASTM D790
0.172 GPa

@Temperature -40.0 °C

24.9 ksi

@Temperature -40.0 °F

ISO 178懸壁梁缺口沖擊強度NB

@Temperature -40.0 °C

NB

@Temperature -40.0 °F

ASTM D256
NB

@Temperature 23.0 °C

NB

@Temperature 73.4 °F

ASTM D256
NB

@Temperature -40.0 °C

ISO 180/1A
NB

@Temperature 23.0 °C

ISO 180/1A簡支梁無缺口沖擊強度NB

@Temperature -30.0 °C

NB

@Temperature -22.0 °F

ISO 179/1eU
NB

@Temperature 23.0 °C

ISO 179/1eU簡支梁缺口沖擊強度NB

@Temperature -40.0 °C

ISO 179/1eA
NB

@Temperature -30.0 °C

ISO 179/1eA
NB

@Temperature 23.0 °C

ISO 179/1eA電氣性能額定值 (公制)額定值 (英制)測試方法體積電阻率4.00e+12 ohm-cm

@Temperature 23.0 °C

4.00e+12 ohm-cm

@Temperature 73.4 °F

IEC 60093表面電阻3.00e+14 ohm

@Temperature 23.0 °C

3.00e+14 ohm

@Temperature 73.4 °F

IEC 60093介電常數(shù)4.7

@Frequency 1.00e+6 Hz, Temperature 23.0 °C

4.7

@Frequency 1.00e+6 Hz, Temperature 73.4 °F

IEC 60250
4.8

@Frequency 100 Hz, Temperature 23.0 °C

4.8

@Frequency 100 Hz, Temperature 73.4 °F

IEC 60250介電強度18.0 kV/mm

@Temperature 23.0 °C

457 kV/in

@Temperature 73.4 °F

IEC 60243-1耗散因數(shù)0.013

@Frequency 100 Hz, Temperature 23.0 °C

0.013

@Frequency 100 Hz, Temperature 73.4 °F

IEC 60250
0.020

@Frequency 1.00e+6 Hz, Temperature 23.0 °C

0.020

@Frequency 1.00e+6 Hz, Temperature 73.4 °F

IEC 60250相比耐漏電起痕指數(shù)(CTI)>= 600 V

@Temperature 23.0 °C

>= 600 V

@Temperature 73.4 °F

IEC 60112
>= 600 V

@Thickness 3.00 mm, Temperature 23.0 °C

>= 600 V

@Thickness 0.118 in, Temperature 73.4 °F

UL 746A熱性能額定值 (公制)額定值 (英制)測試方法線形熱膨脹系數(shù) - 流動500 μm/m-°C

@Temperature -40.0 - 23.0 °C

278 μin/in-°F

@Temperature -40.0 - 73.4 °F

ASTM E 831
500 μm/m-°C

@Temperature 23.0 - 55.0 °C

278 μin/in-°F

@Temperature 73.4 - 131 °F

ASTM E 831
500 μm/m-°C

@Temperature 55.0 - 120 °C

278 μin/in-°F

@Temperature 131 - 248 °F

ASTM E 831
500 μm/m-°C

@Temperature -40.0 - 23.0 °C

ISO 11359-1/-2
500 μm/m-°C

@Temperature 23.0 - 55.0 °C

ISO 11359-1/-2
500 μm/m-°C

@Temperature 55.0 - 120 °C

ISO 11359-1/-2線性熱膨脹系數(shù),橫向流動190 μm/m-°C

@Temperature 23.0 - 55.0 °C

106 μin/in-°F

@Temperature 73.4 - 131 °F

ISO 11359-1/-2
190 μm/m-°C

@Temperature 55.0 - 120 °C

106 μin/in-°F

@Temperature 131 - 248 °F

ISO 11359-1/-2
192 μm/m-°C

@Temperature 55.0 - 120 °C

107 μin/in-°F

@Temperature 131 - 248 °F

ASTM E 831
219 μm/m-°C

@Temperature 23.0 - 55.0 °C

122 μin/in-°F

@Temperature 73.4 - 131 °F

ASTM E 831
270 μm/m-°C

@Temperature -40.0 - 23.0 °C

150 μin/in-°F

@Temperature -40.0 - 73.4 °F

ISO 11359-1/-2
277 μm/m-°C

@Temperature -40.0 - 23.0 °C

154 μin/in-°F

@Temperature -40.0 - 73.4 °F

ASTM E 831熔融溫度193 °C379 °F10°C/min; ISO 11357-1/-3
193 °C379 °FASTM D3418載荷下熱變形溫度(0.46 MPa)50.0 °C122 °FISO 75-1/-2
55.0 °C131 °FASTM D648脆化溫度-95.0 °C-139 °FISO 974玻璃化轉(zhuǎn)變溫度，Tg-50.0 °C-58.0 °F10°C/min; ISO 11357-1/-2UL RTI50.0 °C

@Thickness 1.50 mm

122 °F

@Thickness 0.0591 in

UL 746B
50.0 °C

@Thickness 3.00 mm

122 °F

@Thickness 0.118 in

UL 746B

分類

聚合物是由許多較小而結(jié)構(gòu)簡單的小分子(monomer)，藉共價鍵來組合而成的。 TPE(01)本色( 30度-120度 ),(02)透明( 30度-120度 ),(03)黑色( 30度-120度 ) ,(04)TPE射粘級 4.TPE 不銹綱級 ,(05)TPE食品級 ,(06)TPE擠出級, (07)TPE片材級 ,(08)TPE阻燃 ,(09)TPE耐磨級, (10)TPE烯烴級 ,(11)TPE阻隔級, (12)TPE導電級 ,(13)TPE改性, (14)TPE吹塑級 ,(15)發(fā)泡級,(16)薄膜級,(17)軟膠級